Polypropylene cracked film industrial wire (commonly known as fishing net wire, cracked film wire) is an industrial material made of polypropylene fiber by special process, and its identification needs to be combined with physical properties, process characteristics and professional testing methods. The following is a comprehensive identification method based on multi-dimensional information:
I. Physical property observation method
Appearance and form
Color and luster: High quality polypropylene film filament is usually beige or custom color, the surface matte sense is obvious, the longitudinal surface of the fiber is flat and smooth, and the cross-section is circular. Poor quality products may appear gray or speckled with impurities due to recycled material doping.
Fiber structure: Split film filament is divided into mesh fibril by stretching polypropylene film, forming a unique "split film" texture, feel soft but tough texture, which is different from the uniform smooth surface of ordinary polypropylene filament.
Density test
Polypropylene is the lightest of the common chemical fibers, with a density of only 0.91g/cm, much lower than polyester (1.38g/cm). Through the floating test, it can be preliminatively judged that the polypropylene film is floating on the surface, while the polyester and nylon are sinking.
Second, technical parameter detection method
Breaking strength and elongation
The fracture strength of high-quality cracked film wire should be ≥4.0cN/dtex, and the elongation at break should be controlled in the range of 5%-8%. For example, the dry heat shrinkage rate of 840D cracked film filament (132℃, 15 minutes) should be less than 6%, if the measured value is high, it may be doped with low molecular weight polypropylene.
Reference standard: The linear density deviation rate should be less than 5%, if it exceeds this range, the production process may be unstable or the raw material is unqualified.
Chemical resistance
Polypropylene split film filament has good tolerance to acid and alkali (except concentrated nitric acid and concentrated caustic soda). The fiber can be immersed in 10% hydrochloric acid or sodium hydroxide solution for 24 hours, if there is no obvious swelling or strength loss, it is genuine.
Third, combustion and thermal stability test
Combustion characteristics
Burning odor: polypropylene film filament burning gives off the smell of oil, the flame is yellow and blue, slowly self-extinguishing after the fire; The combustion residue is a hard round light yellow brown particle, which is easily broken by hand. Polyester burns with an aromatic smell, leaving white clumps.
Thermal shrinkage rate: the dry heat shrinkage rate of the cracked film filament at high temperature (such as 132℃) should be less than 8%, if the shrinkage rate is too high, it may be due to the processing temperature is out of control or the raw material molecular weight is insufficient.
Xuzhou Peace Chemical Fiber Co., Ltd. is located in Xuzhou, Jiangsu. It has focused on the research and development and production of polypropylene, high strength, high strength, high strength, high strength, anti-aging, acid and alkali resistant, etc., which also make polypropylene high strength. Wire can be applied to all aspects of our lives. Peaceful chemical polypropylene, manufacturers supply, complete products, high quality after-sales service, users can rest assured to buy. Peace chemical fiber also has a polypropylene industrial silk, polypropylene high strength wire, high-strength polypropylene wire, polypropylene high strength yarn, high-strength propylene, and hydrazine industrial wire.